ISARD 3180 second-gen PO encapsulation film

ISARD 3180 polyolefin elastic encapsulation film is a cross-linked composite polyolefin PV encapsulating material that is produced by mixing polyolefin copolymer resin with various necessary additives in certain mixing ratio. It is characterized by excellent moisture insulation, the ability to firmly bind the glass and backsheet durably, the ability to protect and fix solar cells, excellent resistance to dampness, heat and ultraviolet ageing, and long stable resistance to PID.

Characteristic Value

NO.	Performance	Test Item	Standard Value	Unit	ISARD 3180
1	Physical Properties	Thickness	GB/T 6672-2001	mm	0.4~0.8
		Tensile strength (After lamination)	GB/T 13022-91	Mpa	≥8
		Ultimate Elongation (After lamination )		%	≥400
		Peel Strength with Glass	ASTM D903	N/cm	≥70
		Peel Strength with Back Sheet		N/cm	≥40
2	Thermal Properties	MD/TD shrinkage	ASTM 1204	MD%/TD%	≤4/≤2
3		Gel content	ASTM D2765	％	≥70%
4	Electrical Properties	Volume resistivity	GB 1410-89	Ω .cm	≥1.0×1015
5		Light transmission after lamination (280- 380nm)	GB/T 2410- 2008	%	≤20
6	optical properties	Light transmission after lamination (380nm~1100nm)	GB/T 2410- 2008	%	≥90
		UV aging Yellowness Index(60kWh/m2 )	GB/T 29848	ΔYI	≤5
7	Durability	Heat/Humidity85℃/85 aging 1000h	GB/T 29848	ΔYI	≤5

Product Characteristics

1.Can effectively prevent the risk of PID components.

2.Superior weather resistance (including high temperature, high humidity, UV, etc.)

3.Excellent adhesion retention after aging

4.The best light transmittance, to ensure the efficiency of power generation components

5.Lower shrinkage, to ensure the quality of laminated stability

Packaging Mode

1.Tube diameter: 76mm

2.Outer packing for special pressure-resistant carton, transport at the bottom of the tray and stretched with a fixed film, 1 roll / box.

Stock code:688560

Address: No. 32 Jingfa Avenue, Economic and Technological Development Zone, Yichun City, Jiangxi Province

Service hotline

0795-7029699

WeChat official account

Shanghai ICP No. 19026278-1